Anti-stripping High Alumina Brick for Cement Kiln from China manufacturer

Anti-stripping High Alumina Brick for Cement Kiln

Price:	130.0 USD
Payment Terms:	T/T,L/C
Place of Origin:	Henan, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: CN007

Production Capacity: 310,000 tons per year

Delivery Date: about 45-60 days

Al2O3 %: ≥75

Bulk Density: 2.65-2.85g/cm3

Creep Rate: ≤0.8%

Means of Transport: Ocean

Packing: in wooden pellet

Brand Name: CUNSE

Apparent Porosity %: ≤20

Compress Strength: ≥60Mpa

Permanent Linear Change %: 0.1-0.2

1. 11 production lines.
2. Professional sales team and after sales service.
3. Free sample provided if need.

Low Creep High Alumina Brick for Hot-blast Stove

Characteristics:

1: The content of AL2O3 is ≥50%.

2: High refractoriness under load. The RUL is higher than fireclay brick as the high content of Al2O3, however, it is lower than silica brick because of mullite crystal does not form reticular tissue.

3: Excellent slag resistance. High alumina brick is a kind of neutral refractory material so it enjoys excellent resistance to alkali slag corrosion.

Application:

The main markets for low creep high alumina brick are building lining of hot-blast stove, blast furnace, rotary kilns of cement and so on.

Technical Data:

Item	High Alumina Brick
Item	DRL-155	DRL-150	DRL-145	DRL-140	DRL-135	DRL-130	DRL-127
Al2O3,% ≥	75	75	65	65	65	60	50
Apparent Porosity,% ≤	20	21	21	22	22	22	23
Bulk Density, g/cm3	2.65-2.85	2.65-2.85	2.50-2.70	2.40-2.60	2.35-2.30	2.30-2.50	2.30-2.50
Compress Strength, Mpa ≥	60	60	60	55	55	55	50
Creep Rate, %	1550℃	1500℃	1450℃	1400℃	1350℃	1300℃	1270℃
(0.2Mpa,50h) ≤	0.8	0.8	0.8	0.8	0.8	0.8	0.8
Permanent Linear Change %	1550℃,2h	0.1-0.2	0.1-0.2	--	--	--	--
Permanent Linear Change %	1450℃,2h	--	--	0.1-0.2	0.1-0.4	0.1-0.4	0.1-0.4